| name | trademark | quantity(add) percentage 1000kg | condition | application | package |
| Granular refining agent | M-A | 0.025-0.1% | 730-750℃ | Quickly remove alkali metal {sodium, calcium and lithium} and non-metal oxide impurities in the melt,When used together with inert gas, it can also enhance the degassing function | 2kg/bag 20kg/box |
| Aluminum alloy degassing refining agent | M-B | 0.2-0.5% | >680℃ | This product has excellent degassing performance and can significantly reduce the gas content of aluminum parts. | 0.25kg/piece 20kg/box |
| Aluminium(copper)Alloy slag agent | MC-A | 0.1-0.3% | water<0.5% Particle size 30-50 mesh | Used for non-high magnesium aluminum alloys, suitable for use in furnaces at high temperatures. It has the functions of cleaning and covering the slag on the furnace wall. | 2kg/bag 20kg/box |
| MC-B | 0.1-0.6% | Used for smelting and casting of pure aluminum and aluminum alloys | |||
| MC-C | 0.1-0.15% | Used for smelting sodium aluminum and aluminum alloys and strontium Separation of aluminum slag from deteriorated aluminum-silicon alloy | |||
| MC-D | 0.1-0.3% | Used for copper alloy slag cleaning and refining | |||
| Aluminum alloy covering agent | MD-A | 0.2-0.4% | 700-760℃ | Aluminum alloys other than pure aluminum and high magnesium alloys | 2kg/bag 20kg/box |
| MD-B | 0.2-0.4% | Used for high magnesium alloys since this product does not contain any sadium salt, The sodium salt will not make the alloy "sodium brittle" | |||
| Aluminum alloy refining agent | ME-A | 0.1-0.2% | 730-750℃ | Aluminum alloys other than pure aluminum and high magnesium alloys | 2kg/bag 20kg/box |
| ME-B | 0.1-0.2% | High silicon alloy | |||
| ME-C | 0.1-0.2% | High magnesium alloy | |||
| Zinc alloy refining agent | MF-A reverberatory furnace | 0.2-0.6% | >430℃ | It effectively condenses non-metallic inclusions and protects zinc and zinc-based alloys from oxidation, removing slag inclusions from the metal melt. At the same time, the flux can react with the slag layer to effectively separate the metallic zinc and slag layers. | 2kg/bag 20kg/box |
| MF-B Crucible furnace | 0.5-0.8% | ||||
| Furnace cleaning agent | MG | 8-12kg/m2 | furance temperature>850℃ | Aluminum alloy reverberatory furnace, holding furnace and crucible furnace wall cleaning for gas | 2kg/bag 20kg/box |
| Titanium boron refiner agent | MH | 0.5-2kg/metric ton(AL) | >700℃ | Suitable for grain refinement during melting and casting of pure aluminum and general aluminum alloys. Improve the strength and plasticity of finished aluminum parts and improve overall mechanical properties | 0.5kg/piece 20kg/box |
| element remover agent | MK-NA Aluminum sodium remover | 0.2-0.6% | >720℃ | Limited removal of excess sodium in aluminum alloy, while having good degassing and slag removal effects | 10kg/bag 20kg/box |
| MK-CA Aluminum Calcium recover | (original Ca minus object Ca)%*Al weight*(15-20) | >730℃ | Limited removal of excess calcium in aluminum alloy, while having good degassing and slag removal effects | ||
| MK-MG Aluminum Magnesium recover | (original Mg minus object Mg)%*Al weight*(4-6) | Limited removal of excess magnesium in aluminum alloys, while having good degassing and slag removal effects |